抛丸机磨料:铸钢丸

2 1

20161026190142 2

铸钢砂

111 3

不锈钢丝切丸

钢型 钢号 化学成分
C Cr Ni Mn P S Mo Si Cu N 其他
奥氏体型 201 ≤0.15 16.00-18.00 3.50-5.50 5.50-7.50 ≤0.060 ≤0.030 ≤1.00 ≤0.25
202 ≤0.15 17.00-19.00 4.00-6.00 7.50-10.00 ≤0.060 ≤0.030 ≤1.00 ≤0.25
301 ≤0.15 16.00-18.00 6.00-8.00 ≤2.00 ≤0.065 ≤0.030 ≤1.00
302 ≤0.15 17.00-19.00 8.00-10.00 ≤2.00 ≤0.035 ≤0.030 ≤1.00
304 ≤0.07 17.00-19.00 8.00-10.00 ≤2.00 ≤0.035 ≤0.030 ≤1.00
316 ≤0.08 16.00-18.50 10.00-14.00 ≤2.00 ≤0.035 ≤0.030 2.00-3.00 ≤1.00
马氏体型 430 ≤0.12 16.00-18.00 0 ≤1.25 ≤0.035 ≤0.030 ≤0.75

 

11111 4

金属磨料 5

钢丸粒度分布表

筛网号 英寸 筛网孔径 SAEJ444钢丸
S930 S780 S660 S550 S460 S390 S330 S280 S230 S170 S110 S70
6 0.132 3.35 AllPass
7 0.111 2.80 AllPass
8 0.0937 2.36 ≥90% AllPass
10 0.0787 2.00 ≥97% ≥85% AllPass AllPass
12 0.0661 1.70 ≥97% ≥85% ≤5% AllPass
14 0.0555 1.40 ≥97% ≥85% ≤5% AllPass
16 0.0469 1.18 ≥97% ≥85% ≤5% AllPass
18 0.0394 1.00 ≥96% ≤5% AllPass
20 0.0331 0.850 ≥85% ≤10% AllPass
25 0.0280 0.710 ≥96% ≥85% ≤10%
30 0.0232 0.600 ≥96% ≥85%
35 0.0197 0.500 ≥97%
40 0.0165 0.425 ≥85% AllPass
45 0.0138 0.355 ≥97% ≤10%
50 0.0117 0.300 ≥80%
80 0.007 0.180 ≥90% ≥80%
120 0.0049 0.125 ≥90%
200 0.0029 0.075
GB(单位:mm)  2.8  2.5 2.0  1.7 1.4 1.2 1.0 0.8 0.6 0.4 0.3  0.2

钢丸参数

项目 国家标准钢丸 高质量钢丸
化学成分% 碳  C 0.85-1.20 0.85-1.0
硅  SI 0.40-1.20 0.70-1.0
锰  Mn 0.60-1.20 0.75-1.0
硫  S <0.05 <0.030
磷  P <0.05 <0.030
硬度 钢丸 HRC40-5
HRC55-62
HRC44-48
HRC58-62
密度 钢丸 ≥7.20g/cm3 7.4g/cm3
金相组织 回火马氏体或屈氏体 回火马氏体+贝氏体 复相组织
外观 圆形球
空心颗粒<10%
裂纹颗粒<15%
圆形球
空心颗粒<5%
裂纹颗粒<10%

铸钢砂参数

名称 铸钢砂
化学成分 碳(C) 0.70—1.2%
锰(Mn) 0.60—1.2%
硅(SI) 040—1.2%
硫(S) ≤0.05%
磷(P) ≤0.05%
平均硬度(500g核载下测定)
硬度偏差 最大偏差范围为3.0HRC或40HV
金相组织 均匀的回火马氏体或回火屈氏体+弥散分布碳化物
最下密度(酒精置换法测定) 7.4g/cm³